Summary
Conventional oil well cement cannot hydrate within 24 hours below 5 ℃. The conventional early-strength enhancer is difficult to achieve the desired early strength at this temperature and most contain chloride ion which has a strong corrosion to casing. ZOC-DA92S is a chlorine-free inorganic mixture, which has no corrosive effect on the casing and has a significant early-strength enhancing effect in the temperature range of 3 ℃ ~ 30 ℃ . It is suitable for cementing of deepwater surface casing.
Usage range
Dry mixing or wet mixing, recommend wet mixing with pulp. Pulp water is sea water, or it can be fresh water.
Temperature is 3℃~120℃.
Recommended dosage：0.5~3.0% (BWOC).
Recommended to use with ZOC-DA93L.
Recommended to use with ZOC-DA93L, ZOC-DG72S and ZOC-GS12L in anti shallow stream cementing.
Technical data
Physics and chemistry performance index
|
Item
|
Index
|
|
Appearance
|
Light grey powder
|
|
Density，g/cm3
|
2.0±0.05
|
|
pH，2% aqueous solution
|
7~8
|
|
20 Mesh Residue on Sieve，%
|
≤2
|
Cement slurry performance indicators
|
Item
|
Index
|
|
Thickening Time，min(27℃，15MPa)
|
≤150
|
|
Initial Consistency，BC
|
≤22
|
|
Compressive Strength，MPa（27℃，atmospheric pressure, 24h）
|
≥16
|
|
Slurry composition（1.9 g/cm3）：Class G oil well cement，1% ZOC-DA92S，Seawater.
|
Storage
It should be stored in cool, dry and ventilated areas and avoid being exposed to the sun and rain.
Shelf life:24 months.