Summary
ZOC-410S is a type of fluid loss additive that the main component was AMPS polymers, which has good universality and can be used in a group of slurry system.
The product was suitable for a wide temperature range, and its high temperature resistance up to 230℃. The cement slurry with this product had good fluidity, stability, less free water, noretardedeffect, rapid strength development and has no special need to slurry-mixing water. Used in Both Fresh Water, Salt Water.
Physical and Chemical Properties
|
Item
|
Index
|
|
Appearance
|
White or light yellow powder
|
|
Bulk density, g/cm3
|
0.92±0.20
|
|
Solubility, %
|
100
|
|
Moisture content, %
|
≤5.0
|
Cement SlurryProperties
|
Item
|
Index
|
Test conditions
|
|
Fluid Loss, mL
|
≤50
|
80℃, 6.9MPa
|
|
Thickening Time, min
|
≥60
|
80℃, 45MPa/45min
|
|
Initial Consistency, Bc
|
≤25
|
|
Compressive Strength, MPa
|
≥14
|
80℃, Normal pressure, 24h
|
|
Free Water, mL
|
≤1.0
|
80℃, Normal pressure
|
|
Slurry composition：100% Class G cement (high sulfur resistant), and 44.0% (BWOC) fresh water, and 0.6% (BWOC) ZOC-410S, and 0.5% (BWOC)SX60L。
|
Applications
The recommended operating temperature was below 230℃(BHCT).
The recommended dosage was 0.6-1.5% (BWOC) in Fresh Water & Low Temperature and 0.6%-2.0% (BWOC) in Salt Water & High Temperature.
25kg/bag, or based on custom’s request.