Summary
ZOC-G90S is a type of fluid loss additive that the main component was humic acid and AMPS graft polymers, which has good fluid loss control ability and high strength develop speed and low free water, and it also has good universality and can be used in a group of slurry system.
Features
It can obviously reduce the fluid loss amount, generally can be controlled within 100ml. Increase dosage amount, it can be controlled within 50ml.
Thickening time regularly reduces with the temperature increase. It has no verse effect on cement stone.
Dosage is insensitive, no mutational site. Can be used safely.
Physical and Chemical Properties
|
Item
|
Index
|
|
Appearance
|
Black or brown black powder
|
|
Bulk density, g/cm3
|
0.80±0.20
|
|
Solubility, %
|
100
|
|
Moisture content, %
|
≤5.0
|
|
Rheological property, 90℃
|
Φ3≤15/Φ6≤20
|
|
Fluid loss amount (90℃，6.9MPa，30min), mL
|
≤60
|
|
Cement slurry composition: 100% Grade "G" cement, +44% fresh water +1% water loss control agent, ZOC-G90S+0.25% defoaming agent ZOC-X60L
|
Applications
The recommended operating temperature was below 180℃ (BHCT).
The recommended dosage was 1.0-1.5% (BWOC).
Applicable to high temperature, low density and high density of cement slurry system mix with every level of oil well cement and admixture in the definition of APISpec10A (such as silica fume, cenosphere, fly ash, slag, bentonite and barite powder and iron powder, etc.)
It can be used in conjunction with medium temperature retarder ZOC-H100L, high temperature retarder ZOC-H50L, early strength agent ZOC-A90S, dispersant ZOC-F45L, and also can be used alone.
Storage
Keep in a cool, cool and dry environment. Avoid sun and rain.
Shelf life is 12 months.
25kg three in one composite bags, or packaged according to customer requirements.